A preliminary investigation of the effects of environmentally assisted cracking on natural gas transmission pipelines /
| Main Author: | |
|---|---|
| Other Authors: | |
| Format: | Thesis eBook |
| Language: | English |
| Published: |
[College Station, Tex.] :
[Texas A&M University],
[2005]
|
| Subjects: | |
| Online Access: | Link to OAK Trust copy |
| Abstract: | Concepts for the development of a model to predict natural gas transmission pipeline lifetime in a corrosive environment are constructed. Primarily, the effects of environmentally assisted cracking (EAC) are explored. Tensile test specimens from a sample of API 5L X-52 pipeline were tested in a simulated groundwater solution and subsequently analyzed. The results suggested that the simulated environment ultimately reduced the ductility of the test specimens; however, no evidence of "classical" stress corrosion crack morphology was discovered. However, corrosion pits up to 0.75 mm (0.03 in) were revealed during metallographic analysis. A Marin factor analogy and an energy method concept are suggested and explored. Ultimately, the test data set was too small for the results to be of any directly applicable significance. |
|---|---|
| Item Description: | "Major Subject: Mechanical Engineering" Title from author supplied metadata (automated record created on Sep. 21, 2005.) Vita. Abstract. Electronic resource. |
| Format: | Mode of access: World Wide Web. System requirements: World Wide Web access and Adobe Acrobat Reader. |
| Bibliography: | Includes bibliographical references. |