Fabrication of NiTi shape memory alloy from elemental powders by hot isostatic pressing /
900-1050 'C, and machined to expose a gauge section of
| Main Author: | |
|---|---|
| Format: | Thesis eBook |
| Language: | English |
| Published: |
[Place of publication not identified] :
[publisher not identified] ;
1997.
|
| Subjects: | |
| Online Access: | Link to OAKTrust copy |
| Summary: | 900-1050 'C, and machined to expose a gauge section of a procedure for producing cylindrical specimens of NiTi shape and 50.6at.% Ni, packed and sealed into stainless steel behavior were measured. Specimens of approximately 99% consolidated NiTi material for thennomechanical testing. containers, hot isostatically pressed (HIPed) at 20OMPa and determine transfor-nation temperatures as well as for hot isostatic pressing. Powders were mixed to ratios of 50.0 mechanically tested in tension and compression and were shown memory alloy for mechanical testing from elemental powders by microscopic examination. Effects of post-consolidation heat microstructures were produced. The specimen were Some samples of material were used for DSC analysis to The research involved in this thesis was conducted to develop theoretical density and nearly homogeneous NiTi to exhibit shape memory properties. treatments on the material microstructure and transformation |
|---|---|
| Item Description: | "Major subject: Aerospace Engineering". Vita. |
| Physical Description: | xiv, 137 leaves : illustrations ; 28 cm. Also available online. Issued also on microfiche from Lange Micrographics. |
| Bibliography: | Includes bibliographical references: pages 128-131. |