Synthesis and characterization of new cystalline titanates /
5, and hydrous crystalline silicon titanates, labeled as TAM-
| Main Author: | |
|---|---|
| Format: | Thesis eBook |
| Language: | English |
| Published: |
[Place of publication not identified] :
[publisher not identified] ;
1994.
|
| Subjects: | |
| Online Access: | Link to OAKTrust copy |
| Summary: | 5, and hydrous crystalline silicon titanates, labeled as TAM- 7 and 8, on their physical and catalytic properties was the calcination at 500 'C. Although pillaring the titanates, by characterization purposes, the effect of the synthesis characterized by atomic adsorption, X-Ray diffraction, conditions was also studied by varying the reaction differential thermal analysis. By swelling and pillaring, Dosch (1 990) and Anthony et al. (I 992). Prior to scaling employing n-alkylanline and inorganic compounds, did improve for 24 hours. hydrous crystalline titanates, labeled as the Types 3, 4 and layered materials had been reported previously by Anthony and main objective of this research. The synthesis of these sensitive to the synthesis conditions. Catalysts were sorption measurements, thermal gravimetric analysis and temperature and time. These titanates were found to be very the catalytic activity and the stability of the titanates. The determination of the effect of swelling and pillaring of the interlayer distance was increased up to 2.6 nm prior to the structures changed substantially when calcined at 500 'C the synthesis from 3 grams to 100 grams batches for |
|---|---|
| Item Description: | "Major subject: Chemical Engineering". Vita. |
| Physical Description: | xiii, 149 leaves : illustrations ; 28 cm. Also available online. |
| Bibliography: | Includes bibliographical references. |